POLYMER EMULSIONS
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH (±1.0) |
Viscosity
(mPas Spindle/rpm) (BROOKFIELD RV-DV II at 25 °C) |
Tg ( °C) |
Application |
|
|
ARAKRIL ADC 250 |
S/AC |
50.0 |
8,0 |
8000-11000 |
(5/20) |
TG
19 +/-2 |
Polymer emulsion having high scrub resistance and good pigment binding capacity for
interior & exterior paints, primers, putties, high PVC paints, textured coatings |
|
ARAKRIL ADC 750 |
S/AC |
50.0 |
8,0 |
8000-11000 |
(5/20) |
TG
18 +/-2 |
Polymer emulsion having high scrub resistance and good pigment binding capacity for
interior & exterior paints, primers, putties, high PVC paints, textured coatings BASF NS296D Offset. |
|
ARAKRIL ADC 777 |
S/AC |
50.0 |
8,0 |
8000-15000 |
(5/20) |
Low particle sized polymer emulsion having superior water resistance properties for water-proof systems, exterior paints, architectural finishes | |
|
ARAKRIL ADC 500 |
S/AC |
50.0 |
8,0 |
11000-14000 |
(5/20) |
TG
19 +/-2 |
High viscosity polymer emulsion for interior & exterior high PVC paints, mineral & textured coatings, plasters, exterior insulation and finishing systems (EIFS) |
|
ARAKRIL ADC 900 LVA |
S/AC |
50.0 |
8,0 |
1000-2500 |
(3/20) |
TG
20 +/-2 |
Low viscosity polymer emulsion for interior& exterior high PVC paints, mineral & textured
coatings, plasters |
|
ARAKRIL ADC 450 SLC |
S/AC |
50.0 |
8,0 |
8000-20000 |
(5/20) |
TG
4 +/-2 |
Soft polymer emulsion for exterior/interior high PVC paints, mineral & textured coatings, plasters |
|
ARAKRIL ADC 330 NA |
S/AC |
50.0 |
8,0 |
1000-2000 |
(3/20) |
TG
18 +/-2 |
Ammonia free medium hard polymer emulsion having good pigment binding capacity for interior &
exterior paints, primers, textured coatings |
|
ARAKRIL ADC 5030 |
S/AC |
30.0 |
8,0 |
Max 100 |
(2/30) |
NANO-SIZED polymer emulsion for the manufacture of deep primers and wood stains. | |
|
ARAKRIL ADC 5034 |
S/AC |
34.0 |
8,0 |
Max 100 |
(2/30) |
NANO-SIZED polymer emulsion for the manufacture of deep primers and wood stains. | |
|
ARAKRIL ADC 6030 |
S/AC |
30.0 |
8,0 |
Max 100 |
(2/30) |
NANO-SIZED polymer emulsion for the manufacture of deep primers and wood stains. | |
|
ARAKRIL ADC 6034 |
S/AC |
34.0 |
8,0 |
Max 100 |
(2/30) |
NANO-SIZED polymer emulsion for the manufacture of deep primers and wood stains. | |
|
ARAKRIL DC 938 |
V/AC |
50.0 |
4,5 |
1000-4000 |
(5/20) |
Medium hard polymer emulsion having non-yellowing properties for interior paints, textured coatings,
primers. |
|
|
ARAKRIL DC 2053 REPLACED BY DC 3055 |
V/AC |
55.0 |
4,5 |
MAX 1000 |
(5/20) |
TG
10 +/-2 |
Medium hard polymer emulsion having non-yellowing properties for interior paints,
textured coatings, primers. |
|
ARAKRIL DC 58 |
V/AC |
58.0 |
5,0 |
2000-5000 |
(3/20) |
TG
20 +/-2 |
Medium hard polymer emulsion having non-yellowing properties for interior paints,
textured coatings, primers. |
|
ARAKRIL VVA 150 Replaced VVA-50 |
V/V |
50.0 |
4,0 |
500-5000 |
(5/20) |
TG
28 +/-2 |
Polymer emulsion for interior & exterior paints, plasters & primers, textured coatings,
high PVC paints |
|
ARAKRIL VVA 155 |
V/V |
55.0 |
4,0 |
500-5000 |
(5/20) |
TG
29 +/-2 |
Polymer emulsion for interior & exterior paints, primers, textured
coatings |
|
ARAKRIL AK 501 |
P/AC |
45.0 |
9,0 |
10000-20000 |
(5/20) |
TG
16 +/-2 |
High viscosity polymer emulsion for masonry paints & indoor paints |
|
ARAKRIL AK 550 |
P/AC |
50.0 |
8,0 |
5000-10000 |
(5/20) |
TG
16 +/-2 |
Medium hard polymer emulsion having high viscosity and high scrub resistance for interior &
exterior paints |
|
ARAKRIL AK 505 |
P/AC |
50.0 |
9,0 |
Max 400 |
(2/30) |
TG
16 +/-2 |
Low viscosity polymer emulsion having superior scrub resistance for exterior/interior, semi-gloss and
eggshell paints, primers |
|
ARAKRIL AK 561 |
P/AC |
50.0 |
8,0 |
Max 500 |
(2/60) |
Wet adhesion promoted polymer emulsion for exterior paints, having excellent wet and dry adhesion
to aged alkyd paints, masonry, wood and metal substrates |
|
|
ARAKRIL AK 308 NA |
P/AC |
50.0 |
8,0 |
Max 1000 |
(3/50) |
TG
8 +/-2 |
Ammonia free medium hard polymer emulsion for exterior/interior high PVC paints mineral & textured
coatings, plasters |
|
ARAKRIL AK 508 |
P/AC |
46.0 |
8.0 |
Max 600 |
( 2 /30 ) |
TG
19 +/-2 |
Excellent hydrophobic binder for exterior/interior, eggshell, matt and gloss paints, wood applications
with adhesion on alkyds. |
|
ARAKRIL AK 48 |
P/AC |
48.0 |
8.0 |
2000-8000 |
(5/20) |
Excellent hydrophobicity, bright, soft and transparent film for marble coatings, outstanding blushing
resistance, very compatible with pigments and fillers. |
|
|
ARAKRIL AK 698 |
P/AC |
45.0 |
7.5 |
Max 800 |
(3/60) |
TG
30 +/-2 |
Emulsion for high gloss enamels with excellent appearance for high- gloss exterior/ interior paints,
topcoats for metal and wood surfaces. |
|
ARAKRIL AK 506 |
P/AC |
50.0 |
8.0 |
Max 1500 |
(2/30) |
TG
0 +/-2 |
Ammonia and formaldehyde free polymer for matt & sheen paints, high PVC paints and masonry paints. |
CONSTRUCTION
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH (±1.0) |
Viscosity
(mPas Spindle/rpm) (BROOKFIELD RV-DV II at 25 °C) |
Tg ( °C) |
Application |
|||
|
ARAKRIL STA 565 |
S/AC |
50.0 |
8.0 |
4000 – 11000 |
(5/20) |
TG
-7 +/-2 |
Elastic, excellent hydrophobic copolymer for roof coatings moisture barrier coatings, exterior insulation and finishing systems (EIFS),crack fillers, caulks. | ||
| ARAKRIL STA 565 SL | S/AC | 50.0 | 8,0 | 4000-11000 | (5/20) | TG
-7 +/-2 |
(TG = -7+/-2) Emulsion for sealants, roof coatings, moisture barrier coatings, crack fillers, caulks high with tensile strength and superior flexibility. BASF Acronal NS567 Offset. | ||
|
ARAKRIL |
STA |
765 S |
S/AC |
50.0 |
8.0 |
5000 – 15000 |
(5/20) |
Silanated flexible binder for roof coatings, moisture barrier coatings tile adhesives, exterior insulation and finishing systems (EIFS), caulks, sealants. | |
| ARAKRIL | STA | 357 | S/AC | 57.0 | 8.0 | Max 1500 | (3/100) | TG
-6 +/-2 |
(TG = -6) Binder for tile adhesives, two component mortars, cement modifiers, insulating coatings with cement and flat roof coatings and moisture barrier coatings. BASF Acronal NS400 Offset. |
| ARAKRIL | STA | 458 | S/AC | 58.0 | 8.0 | Max.1000 | (3/100) | Binder for tile adhesives, two component mortars, insulating coatings with cement and flat roof coatings and moisture barrier coatings. | |
|
ARAKRIL VAT 711 |
S/AC |
50.0 |
6.0 |
Max 350 |
(2/30) |
TG
-31 +/-2 |
(TG = -31+/-2) Plasticizer and formaldehyde free cement modifier flexible polymer for sealants, pasty tile adhesives, roof coatings and mastics with perfect adhesion and durability. Rhoplex MC-76 offset. | ||
| ARAKRIL ADC 750 | S/AC | 50.0 | 8,0 | 8000-11000 | (5/20) | TG 18 +/-2 | (TG = 18+/-2) Polymer emulsion having high scrub resistance and good pigment binding capacity for interior & exterior paints, primers, putties, high PVC paints, textured coatings BASF NS296D Offset. | ||
| ARAKRIL AK 965 | P/AC | 65.0 | 8,0 | Max. 1000 | (5/20) | TG -40 +/-2 | Emulsion for sealants, roof coatings, moisture barrier coatings. Low temperature flexibility with ageing resistance and excellent stability | ||
|
ARAKRIL DC 865 |
V/AC |
65.0 |
8,0 |
Max. 1000 |
(5/20) |
Emulsion for sealants. Excellent adhesive properties and improved drying efficiency at high application speeds with elastic and low temperature flexibility | |||
Yellow = currently stocked in U.S.
ELASTOMERICS
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH (±1.0) |
Viscosity
(mPas Spindle/rpm) (BROOKFIELD RV-DV II at 25 °C) |
Tg (ºC) |
Application |
|
|
ARAKRIL AK 840 · See AK 827 |
P/AC |
55.0 |
8,0 |
20-500 |
(5/20) |
TG -40 +/-2 |
* Replace stock with AK 827 (See below) |
|
ARAKRIL AK 827 |
P/AC |
55.0 |
8,0 |
20-500 |
(5/20) |
TG -27 +/-2 |
(TG = -27+/-2) UV resistant, high alkali, dirt pick-up and blister resistance with excellent flexibility at low temperatures. Excellent adhesion when applied over various roofing substrates including metal, concrete, aged built-up asphalt, bitumen membrane and P/U foam. EC1791 Offset |
|
ARAKRIL AK 965 |
P/AC |
65.0 |
8,0 |
Max. 1000 |
(5/20) |
TG -40 +/-2 |
Emulsion for sealants, roof coatings, moisture barrier coatings. Low temperature flexibility with ageing resistance and excellent stability |
|
ARAKRIL DC 865 |
V/AC |
65.0 |
8,0 |
Max. 1000 |
(5/20) |
TG -30 +/-2 |
Emulsion for sealants. Excellent adhesive properties and improved drying efficiency at high application speeds with elastic and low temperature flexibility |
WOOD COATING
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH (±1.0) |
Viscosity
(mPas Spindle/rpm) (BROOKFIELD RV-DV II at 25 °C) |
Tg (ºC) |
Application |
|
| ARAKRIL ADC 43 W | S/AC | 43.0 | 8.0 | Max 700 | ( 2 /60 ) | Plasticizer free acrylic binder for wood surface coatings with high resistance to water and household chemicals | |
| ARAKRIL AK 45 W | P/AC | 45.0 | 8.0 | Max 1000 | (3/100) | Wood surface coating with high blushing, stain, alkalinity and blocking resistance, wet adhesion. | |
|
ARAKRIL AK 698 |
P/AC |
45.0 |
7.0 |
Max 800 |
( 3 /60 ) |
TG
30 +/-2 |
“High-gloss exterior and interior paints, topcoats for metal and wood surfaces, Excellent adhesion for wet and dry aged alkyds, galvanized steel and PVC surfaces and excellent scrub resistance.” |
|
ARAKRIL AK 561 |
P/AC |
50.0 |
8.0 |
Max 500 |
( 2 /60 ) |
High performance, formaldehyde free interior paints, high adhesion, good scrub and UV resistance, applicable for masonry paints, forming very hydrophobic, bright, transparent and medium hard film. | |
|
ARAKRIL AK 508 |
P/AC |
46.0 |
8.0 |
Max 600 |
( 2 /30 ) |
TG
19 +/-2 |
Binder for exterior/interior, eggshell, matt and gloss paints , wood applications with adhesion on alkyds. Suitable for interior masonry paints, wood stains and floor paints. |
ADDITIVES
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH (±1.0) |
Viscosity
(mPas Spindle/rpm) (BROOKFIELD RV-DV II at 25 °C) |
Application |
|
| ARPOL 440 N | P/AC | 40.0 | 8.0 | Max 600 | ( 2 /60 ) | Sodium salt of polyacrylic acid, low molecular weight dispersing agent for all types of inorganic fillers and pigments. |
| ARPOL 440 A | P/AC | 40.0 | 8.0 | Max 600 | ( 2 /60 ) | Ammonium salt of polyacrylic acid, low molecular weight dispersing agent for water based systems and inorganic pigments. |
| ARPOL 445 N | P/AC | 45.0 | 8.0 | Max 600 | ( 2 /60 ) | High solid, sodium salt of polyacrylic acid, low molecular weight dispersing agent for all types of inorganic fillers and pigments. |
| ARPOL 445 A | P/AC | 45.0 | 8.0 | Max 600 | ( 2 /60 ) | High solid, ammonium salt of polyacrylic acid, low molecular weight dispersing agent for water based systems and inorganic pigments. |
| ARAKRIL K 20 | P/AC | 30.0 | 3.0 | Min 10000 | (5/20) | General purpose acrylic thickener, hydrophobically-modified alkali- swell able emulsion (HASE) |
| ARAKRIL K 29 | P/AC | 28.0 | 2.5 | Min 3000 | (3/12) | General purpose acrylic thickener, alkali-swell able emulsion (ASE) |
| ARAKRIL KA 28 | P/AC | 28.0 | 2.5 | Min 3000 | (3/12) | General purpose acrylic thickener, alkali-swell able emulsion (ASE),pseudo plastic motion |
MULTI PURPOSE ADHESIVES
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH (±1.0) |
Viscosity
(mPas Spindle/rpm) (BROOKFIELD RV-DV II at 25 °C) |
Application |
|
| ARAKRIL AS 300 | V/AC | 44.0 | 4,0 | 20-200 | ( 7 / 30 ) | It is widely used in cellophane area due to its excellent adhesion property. It is also suitable for paper lamination adhesives. |
| ARAKRIL AS 865 | V/AC | 45.0 | 4,0 | max. 1000 | ( 2 / 50 ) | Emulsion for cellophane & paper lamination adhesive |
| ARAKRIL VM 403 | P/VAc | 50.0 | 4,0 | 40000-100000 | ( 7 / 30 ) | High quality, general purpose wood adhesive with strong adhesion |
|
ARAKRIL VT 99 Y |
P/VAc |
48.0 |
4,0 |
30000-80000 |
( 7 / 30 ) |
Emulsion for adhesive systems. It is widely used for wood and paper adhesives with high viscosity. Textile Lamination is another field to be used |
|
ARAKRIL VT 305 |
P/VAc |
45.0 |
4,0 |
5000-15000 |
( 5 / 20 ) |
Emulsion for adhesive systems. It is widely used for wood and paper adhesives with high viscosity. Textile Lamination is another field to be used |
| ARAKRIL VT 92 Y | P/VAc | 50.0 | 4,0 | max.20000 | ( 6/ 20 ) | Emulsion for wood adhesives to provide extra strong adhesion |
| ARAKRIL VT 93 Y | P/VAc | 50.0 | 4,0 | max.30000 | ( 6/ 20 ) | Emulsion for wood adhesives to provide extra strong adhesion |
PRESSURE SENSITIVE ADHESIVES
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH (±1.0) |
Viscosity
(mPas Spindle/rpm) (BROOKFIELD RV-DV II at 25 °C) |
Application |
|
|
ARAKRIL PSA 180 |
P/AC |
53.0 |
9.0 |
50-400 |
(4/100) |
High quality, a ready-to-use pressure sensitive aqueous acrylic emulsion for manufacture of low noise BOPP pressure sensitive adhesives Has excellent adhesive properties with unique balance of peel, shear, tack and improved drying efficiency at high application speeds. |
|
ARAKRIL PSA 190 |
P/AC |
55.0 |
9.0 |
50-400 |
(4/100) |
High quality, a ready-to-use pressure sensitive aqueous acrylic emulsion for manufacture of BOPP pressure sensitive adhesives Has excellent adhesive properties with unique balance of peel, shear, tack and improved drying efficiency at high application speeds. |
| ARAKRIL PSA 40 E | P/AC | 40.0 | 9.0 | Max. 100 | (4/100) | High quality, a ready-to-use pressure sensitive acrylic emulsion for masking tapes |
| ARAKRIL PSA 150 | P/AC | 50.0 | 7,5-8,5 | Max. 400 | (4/100) | High quality, a ready-to-use pressure sensitive aqueous acrylic emulsion for protective films |
| ARAKRIL PSA 250 | P/AC | 50.0 | 5.0 | Max. 600 | (4/100) | High quality, a ready-to-use pressure sensitive aqueous acrylic emulsion for protective films |
|
ARAKRIL PSA 200 |
P/AC |
60.0 |
4.0 |
Max. 600 |
(4/100) |
High quality, a ready-to-use pressure sensitive aqueous acrylic emulsion for manufacture of label. Has excellent adhesive properties with unique balance of peel, shear, tack and improved drying efficiency at high application speeds. |
|
ARAKRIL PSA 260 |
P/AC |
60.0 |
3,0-7,0 |
Max. 800 |
(4/100) |
High quality, a ready-to-use pressure sensitive aqueous acrylic emulsion for manufacture of label. Has excellent adhesive properties with unique balance of peel, shear, tack and improved drying efficiency at high application speeds. |
PAPER
|
Product Name |
Chemical Composition |
Total Solids (% ±1) |
pH |
Viscosity Brookfield RVDV-II (mpas) |
Application |
| ARAKRIL PCL 05 | S/AC | 50.0 | 4,0-7,0 | max. 600 | Impregnate paper sheets that are used in the manufacture of decorative laminates, wallpapers and filters. |
| ARAKRIL PCL 06 | S/AC | 50.0 | 7,0-9,0 | max. 600 | Impregnate paper sheets that are used in the manufacture of decorative laminates, wallpapers and filters. |
| ARAKRIL PCL 07 | S/AC | 50.0 | 4,0-7,0 | max. 4000 | Impregnate paper sheets that are used in the manufacture of decorative laminates, wallpapers and filters. |
LEGEND
| S/AC : Styrene Acrylic Copolymer | APEO : Alkyl Phenol Ethoxylate |
| V/AC : Vinyl Acrylic Copolymer | Tg (°C) : Glass Transition Temperature |
| P/AC : Pure Acrylic Copolymer | MFFT (°C) : Minimum Film Forming Temperature |
| V/V : Vinyl Acetate / Veova | Viscosity (mPas) : Brookfield RV-DV II at 25°C |
| P/VAc : Polyvinylacetate Homopolymer | N/A : Not Applicable |
| AA/MLA : Acrylic Acid/Maleic Acid Copolymer |
This information is based on our current knowledge and experience. It is not guaranteeing specific properties of the products described or their suitability for a particular application. The prospective user should apply the products to their own investigations and determine the suitability of the materials before adapting them on a commercial scale. Any information given in this catalogue may change without prior notice.
Argon Product, Types of Acrylic Countertypes:
| COUNTERTYPE PRODUCTS FOR ARGON EMULSIONS | ||||||||||
ARGON PRODUCT |
TYPE OF ACRYLIC |
DOW |
BASF |
Neocar/Arkema |
Lipacryl |
HB Fuller |
Air Products |
Specialty Polymers |
Vinavil |
Organik Kimya |
| AK 561 | Pure | Primal AC-261, Rhoplex Multilobe 200 | ||||||||
| DC 2053 | 2535 (Arkema) ? | |||||||||
| DC 58 | Vinyl | Avicor 7448 | PD 0124 | Flexbond 325 | ||||||
| AK 508 / AK561 | Pure | Rhoplex AC 2500 | ||||||||
| AK 550 | Pure | Acronal Optiv 110, 4110 | ||||||||
| AK 506 | Pure | Rhoplex AC 2235M | ||||||||
| ADC 750 | Styrene | Acronal 296 D | Raykote 1515 | 4723 NA(DS) | PST 50 | |||||
| STA 565 SL / STA 565 | Styrene | Rhoplex 2019 RX | Acronal NS 567 D | RayFlex 765 | PST 65 | |||||
| AK 506 | Pure | Rhoplex AC 464 | ||||||||
| AK 840 / AK827 | Pure | Rhoplex EC 1791, MB 3640, 2438C | Acronal Optive 510 | MB 3640 | ||||||
| AK 810 | Pure | Rhoplex EC 2540 | ||||||||
| AK 968 | Pure | Rhoplex SG 20 | Joncryl 537 | |||||||
| AK 938 | Vinyl | Rovace 9100 | PD 0128 | |||||||
| VVA 50 | Veona | |||||||||
| VVA 100 | Veona | |||||||||
| STA 357 | Styrene | Encor 123 (Arkema) | ||||||||
| VAT 711 | Styrene | Rhoplex MC-76, Rhoplex MC-1834P | ||||||||
| Vinyl/Veona | encor 379g | Arkema 379G | ||||||||
| DC 50 | 820 | |||||||||
| DC100 | 850 | |||||||||